Ripening of the AlSi9Cu3ZnMg alloy - mechanical and microstructural characterisation
Abstract
Recovered aluminium has poor mechanical properties, to improve them considerably, three main factors have been considered. The first is to add four very low-density elements to the recovered aluminium, including 9% silicon, 3% copper and some traces of zinc and magnesium less than 1% (≤ 1% Zinc, ≤ 1% Mg), which produces the non-standardized casting alloy AlSi9Cu3ZnMg. Then, in order to obtain a fine microstructure, a gravity die-casting is carried out in the as-cast state noted: F. Finally, to further increase the strength of the F-state and essentially obtain high elasticity stresses, high rigidity modulus with low deformations, the AlSi9Cu3ZnMg alloy composed of 60% scrap and 40% new ingots, is subjected to structural hardening by varying the ripening time for 24 hours in increments of 2 hours, thus giving rise to precipitates of various kinds which impede the dislocations sliding.
The results thus obtained show that the cured state for 12 hours (M12h) is a good compromise between good strength and maximum ductility.
Keywords
Full Text:
PDFReferences
- A. Hakem. Effet du monde d'élaboration et de moturation sur les proprietes mecaniques et la microstructure des alliages de fonderie AL SI. Thèse de doctorat. Universite Mouloud MAMMERI Tizi-Ouzou, Algerie 2014.
- M. Colombié, D. Albert, Matériaux industriels: Matériaux métalliques. Dunod, 2000.
- J.-P. Baillon, J.-M. Dorlo, Des Matériaux. Ecole Polytechnique de Montréal, Montréal, 2000.
- D. François, Essais mécaniques et lois de comportement. Hermès, (2001).
- A. Cornet, F. Hlawka, Propriétés et comportements des matériaux: du microscopique au macroscopique. Ellipses, 2010.
- D.R. Askeland, The science and engineering of materials. Third Edition ed.: PWS Publishing Company Boston, 2003.
- M.F. Ashby, D.R. Jones, Y. Brechet, J. Courbon, M. Dupeux, Matériaux: Microstructure et mise en øeuvre. Dunod, 1991.
- F. Condet, A. Reynaud, Atlas der Metallographie von Gusseisen. Editions Techniques des Industries de la Fonderie, (2009).
- M. Garat, A. Le Nézat, M3637 - Moulage des alliages d’aluminium-Moules permanents: coquille, sous pression et apparentés. Techniques de l’Ingénieur, traité Matériaux métalliques, (2013). doi:10.51257/a-v2-m3637.
- M. Garat, M3635 - Fusion des alliages d’aluminium. Techniques de l’Ingénieur, traité Matériaux métalliques, (2012). doi:10.51257/a-v2-m3637.
- R. Portalier, M810A - Fonderie et moulage des alliages d’aluminium. Techniques de l’Ingénieur, traité Matériaux métalliques, (1990). doi:10.51257/a-v2-m3637.
- M. Garat, M4675 - Propriétés des alliages d’aluminium de fonderie. Techniques de l’Ingénieur, traité Matériaux métalliques, (2012). doi:10.51257/a-v2-m3637.
- J.-B. Leblond, P. Germain, Mécanique de la rupture fragile et ductile. Hermès science publications, 2003.
- A. Pokorny, J. Pokorny, M4122 - Fractographie. Macrographies et micrographies. Techniques de l'ingénieur. Matériaux métalliques, (2003) 1-M4122. 14.
- A. Hakem, Influence of ripening on the evolution of mechanical and structural properties of the AlSi12Cu1Mg alloy. J. Mat. Eng. Str. «JMES», 4(4) (2017) 245-257.
- A. Hakem, Influence of the tempering on the evolution of the mechanical characteristics and microstructure of the foundry alloy AlSi7Zn3Cu2Mg. J. Mat. Eng. Str. «JMES», 5(3) (2018) 289-304.
- C. Meyers, Solution heat treatment effects in A357 alloys. AFS Trans, 93 (1985) 741-750.
- Y. Desalos, M1105 - Introduction aux traitements thermiques des métaux et alliages. Techniques de l’Ingénieur, traité Matériaux métalliques, (2003). doi:10.51257/a-v2-m3637.
- Y. Desalos, M1110 - Panorama métallurgique des traitements thermiques. Techniques de l’Ingénieur, traité Matériaux métalliques, (2003). doi:10.51257/a-v2-m3637.
- R. Develay, M1290 - Traitements thermiques des alliages d’aluminium, Techniques de l’Ingénieur, traité Matériaux métalliques. (1986).
- G. Lesoult, M58 - Solidification - Cristallisation et microstructures Techniques de l'Ingénieur. Traité Matériaux métalliques. (1986). doi:10.51257/a-v1-m58.
- A. Hakem, A. Hakem, Y. Bouafia, Study of Behavior and the Damage in Tensile and with the Shock of the Eutectic Alloy AlSi13Mg Unstandardized. Mater. Today: Proc., 2(10, Part A) (2015) 4984-4991. doi:10.1016/j.matpr.2015.10.087.
- D. Bruno, S. Pierre, M240 - Durcissement par précipitation des alliages d’aluminium Techniques de l'Ingénieur. Traité Matériaux métalliques. (1991). doi:10.51257/a-v1-m240.
- J. Lendvai, Precipitation Processes in Age-Hardenable Aluminium Alloys, in Advanced Light Alloys and Composites, R. Ciach, Editor. Springer Netherlands: Dordrecht. (1998), 307-318. doi:10.1007/978-94-015-9068-6_39.
- J.-L. Martin, Dislocations et plasticité des cristaux. Vol. 5. Lausanne: Presses Polytechniques et Universitaires Romandes, 2000.
- Z. Zhuang, Z. Liu, Y. Cui, Dislocation Mechanism-Based Crystal Plasticity, Z. Zhuang, Z. Liu,Y. Cui, Editors, Academic Press. (2019). doi:https://doi.org/10.1016/B978-0-12-814591-3.00001-7.
- J.G. Kaufman, E.L. Rooy, Aluminum alloy castings: properties, processes, and applications. Asm International, 2004.
- C. Vargel, M4661 - Propriétés générales de l'aluminium et de ses alliages. Techniques de l'ingénieur. Matériaux métalliques, (2005).
- J. Barralis, G. Maeder, Précis de métallurgie: élaboration, structures-propriétés et normalisation. 6e édition ed. Paris: Nathan : AFNOR, 1991.
Refbacks
- There are currently no refbacks.
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
ISSN 2170-127X
This work is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License.
Based on a work at http://revue.ummto.dz.